High purity alumina ceramic disc valve/ stainless tap alumina ceramic disk
ceramic valve:
1,90%-95% Alumina Ceramic valve.
2.High intension.
3.Solid-resist,alkali-resistence.
4,Reasonable price.
Specification of the tap ceramic disc:
- OD: 11.5mm---40mm ceramic discs
- The frictional times is 300, 000 to 500, 000
- Rigidity is 84~86 HRA.
- The thickness tolerance is less than 0.05mm, the diameter tolerance is less than 0.05mm.     Â
Technical Data about tap ceramic disc:
| Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â physical analysis sheet for 95%Al2O3: | ||||
| Â | ||||
| Â | Density | g/cm3 | 3.6 | |
| Substance Characteristic | Water Absorption | Â | O | |
| Sinter Temperature | Â | 1710 | ||
| Physical Characteristic | Hardness | HV | ≥12 | |
| Bending Strength | Mpa | ≥310 | ||
| compressive strength | Kgf/cm2 | 25000 | ||
| Elastic Modulus | GPa | 300 | ||
| fracture toughness | Map.m3/2 | 3 to 4 | ||
| Â | Max Using Temperature | Â | 1450 | |
| Thermal Characteristic | Coefficient of Thermal Expansion | 1X 10-6/°C   | 8 | |
| Â | heat-resistant Temperature | T() | 220 | |
| Thermal Conductivity | W/m.k(25-300) | 24 | ||
| Â | Â | 20Â | Â | >1012 |
| Volume Resistance | 100Â | >.cm | 1012-1013 | |
| Electric Characteristic | Â Â | 300Â | >1010 | |
| Dielectric Strength | KV/mm | 18 | ||
| Dielectric Constant | 100MHz(E) | 9.5 | ||
Main advantage of the tap ceramic disc:
95%Al2O3 ceramic discs,mailly applicated to temperature modulatory valve,conversion valve,modulatory valve of surf and massage bathtub,LPG valves
Good hermetical, compressive resistance,flexual resistance,using longevity will be above 500 thousand times.
High purity alumina ceramic disc valve/ stainless tap alumina ceramic disk
ceramic valve:
1,90%-95% Alumina Ceramic valve.
2.High intension.
3.Solid-resist,alkali-resistence.
4,Reasonable price.
Specification of the tap ceramic disc:
- OD: 11.5mm---40mm ceramic discs
- The frictional times is 300, 000 to 500, 000
- Rigidity is 84~86 HRA.
- The thickness tolerance is less than 0.05mm, the diameter tolerance is less than 0.05mm.     Â
Technical Data about tap ceramic disc:
| Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â physical analysis sheet for 95%Al2O3: | ||||
| Â | ||||
| Â | Density | g/cm3 | 3.6 | |
| Substance Characteristic | Water Absorption | Â | O | |
| Sinter Temperature | Â | 1710 | ||
| Physical Characteristic | Hardness | HV | ≥12 | |
| Bending Strength | Mpa | ≥310 | ||
| compressive strength | Kgf/cm2 | 25000 | ||
| Elastic Modulus | GPa | 300 | ||
| fracture toughness | Map.m3/2 | 3 to 4 | ||
| Â | Max Using Temperature | Â | 1450 | |
| Thermal Characteristic | Coefficient of Thermal Expansion | 1X 10-6/°C   | 8 | |
| Â | heat-resistant Temperature | T() | 220 | |
| Thermal Conductivity | W/m.k(25-300) | 24 | ||
| Â | Â | 20Â | Â | >1012 |
| Volume Resistance | 100Â | >.cm | 1012-1013 | |
| Electric Characteristic | Â Â | 300Â | >1010 | |
| Dielectric Strength | KV/mm | 18 | ||
| Dielectric Constant | 100MHz(E) | 9.5 | ||
Main advantage of the tap ceramic disc:
95%Al2O3 ceramic discs,mailly applicated to temperature modulatory valve,conversion valve,modulatory valve of surf and massage bathtub,LPG valves
Good hermetical, compressive resistance,flexual resistance,using longevity will be above 500 thousand times.
Resin For Inside Ink is a non-reactive plasticized polyurethane resin, used for flexographic and gravure printing inks for OPP and polyester film surface printing. It can also be used for some simple composite structures.
Characteristic
1. Good compatibility with nitrocellulose.
2. Good gloss.
3. Anti-caking, cold-resistant.
4. Animal and vegetable oil resistant, water resistant.
5. Good alcohol solubility.
Inside Composite Printing Ink Resin,Steam Resistance Ink Resin,High Solid Content Ink Resin,Resin For Inside Ink,Outstanding Adhesion on Various Plastic Films
XUCHUAN CHEMICAL(SUZHOU) CO., LTD , https://www.xuchuanpu.com